Lupos® GP2100
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mrN0rv_Lupos-GP2100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Applications Electric & Electronic (Housing, Components) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3730 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 97.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.020 | % | |
| Rear Temperature | 220 to 235 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 230 to 245 | °C | |
| Processing (Melt) Temp | 235 to 245 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-657 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| NEFTEKHIM PP 1452R (Z69S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Nypol® PA A3 G30 NTLA010 NR399 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| PLUSTEK PA108 | Polyram Ram-On Industries | Nylon 66/6 | PLUSTEK |
| Kepital® F25-03HT | KEP Americas | Acetal (POM) Copolymer | Kepital® |