Infino CF-3104HF
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mr8tWS_Infino-CF-3104HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High-impact PC/GF material for the high flowablility exterior material of slim mobile phone of GF 10% |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 23 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.30 to 0.50 | % | ASTM D955, ISO 2577 |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.30 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 59.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 2 | 2900 | MPa | ASTM D790 |
| -- 3 | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 93.0 | MPa | ASTM D790 |
| -- 5 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 280 | J/m | ASTM D256 |
| 23°C 7 | 27 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 141 | °C | ASTM D648 |
| Vicat Softening Temperature | 137 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | ||
| 3.20 mm | V-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 to 290 | °C | |
| Front Temperature | 300 | °C | |
| Nozzle Temperature | 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 Z | RTP Company | Nylon 66 | RTP |
| TechnoMid B330 | TechnoCompound GmbH | Nylon 6 | TechnoMid |
| Sylvin 2900-93 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NANCAR® 1041 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Petrotene® PP B3 TZ PRTA011 PH347 MSP | Petropol Industry and Trade of Polymers LTDA | PP Copolymer | Petrotene® PP |