Plaslube® PC / PBT IM 5220 BK
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mqgrmF_Plaslube-PC-PBT-IM-5220-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PC / PBT IM 5220 BK is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 130 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 84.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 290 | J/m | |
| 23°C, 3.18 mm | 690 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 107 | °C | |
| 1.8 MPa, Unannealed | 98.9 | °C | |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 238 to 266 | °C | |
| Middle Temperature | 238 to 266 | °C | |
| Front Temperature | 238 to 266 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 54.4 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.414 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFLAME C V0S 02 S 20 T0 | RIALTI Srl | PP Copolymer | RIALFLAME |
| PRIMALENE WPP693QB | Southern Polymer, Inc. | LLDPE | PRIMALENE |
| Niuk 50GP30 | Shanghai Niuk New Plastic Technology Co., Ltd. | Nylon 66 | Niuk |
| Hifax CB251 | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ THERMOCOMP™ AF004L compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |