Tufpet PBT S1040P
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mpLq5u_Tufpet-PBT-S1040P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT S1040P is a Polybutylene Terephthalate (PBT) material filled with 40% mineral. It is available in North America for injection molding. Important attributes of Tufpet PBT S1040P are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.1 to 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4900 | MPa | ASTM D790 |
| Flexural Strength | 95.1 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.14 | ||
| vs. Metal - Dynamic | 0.080 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 86.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 187 | °C | |
| 1.8 MPa, Unannealed | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.017 | ASTM D150 | |
| Arc Resistance | 127 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.790 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 303 | °C | |
| Middle Temperature | 230 to 303 | °C | |
| Front Temperature | 230 to 303 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® PP2-1000RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| Geon™ Vinyl Packaging Clear OxyPurge | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Packaging |
| Karina IVORY PVC COMPOUND ML-850-WK-IS-FLEX (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Mediprene® 880136-02 | ELASTO | SEBS | Mediprene® |
| TECACOMP® PEEK TRM XG grey 4006 | Ensinger GmbH | PEEK | TECACOMP® |