PRE-ELEC® PA 1411
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | moqUGE_PRE-ELEC-PA-1411.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PA 1411 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. PRE-ELEC® PA 1411 has a very low electrical resistivity. PRE-ELEC® 1411 is meant to be used as masterbatch and blended with PA 6. Typical applications include injection moulded housings, boxes and technical parts. PRE-ELEC® PA 1411 is well suited for applications where the good mechanical properties of polyamide are required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 1.2 to 2.2 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 69.6 | MPa | ASTM D638 |
| Yield | 70.0 | MPa | ISO 527-2 |
| -- | 68.3 | MPa | ASTM D638 |
| 4.00 mm | 68.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break, 4.00 mm | 12 | % | |
| Flexural Modulus (4.00 mm) | 3100 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 6.3 | kJ/m² | ASTM D256 |
| -20°C | 6.0 | kJ/m² | ISO 179 |
| 23°C | 6.0 | kJ/m² | ISO 179 |
| 23°C | 6.3 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | |
| 23°C, 4.00 mm | 6.30 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 104 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 58.9 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 59.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ASTM D1525, ISO 306/A50 3 5 |
| -- | 188 | °C | ASTM D1525, ISO 306/B50 4 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 50 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 300 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC MGS 91 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Flontech® FT-1-GRN | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Gallonprene® GP520-7011 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| RTP 1099 X 137390 | RTP Company | PBT | RTP |
| Sylvin 916VO Orange 551 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |