Diamond ASA S190
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | moCFqk_Diamond-ASA-S190.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond ASA S190 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 200°C/5.0 kg | 0.90 | g/10 min | |
| 230°C/3.8 kg | 2.7 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 35.2 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 1880 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 72.2 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 91.1 | °C | |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 265 | °C | |
| Front Temperature | 235 to 272 | °C | |
| Nozzle Temperature | 220 to 272 | °C | |
| Processing (Melt) Temp | 220 to 272 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7003S | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Tarnoform® 300 FT1,4 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Xuchuan XCW-20N | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Epocast 1610-A1 | Huntsman Advanced Materials | Epoxy | Epocast |
| LNP™ THERMOCOMP™ KF004AL compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ THERMOCOMP™ |