Braskem PE S 1522
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mntpXa_Braskem-PE-S-1522.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: S1522 is a low density polyethylene produced in a high-pressure process, which presents good balance between mechanical properties and processability. Contain no additives. Applications: Blow molded articles for general purpose and injection blow molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 11.0 | MPa | |
| Break, Compression Molded | 12.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 850 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 230 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 110 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon X2500-00 | RheTech, Inc. | Nylon 66 | Rhelon |
| Akulon® K224-HGM35 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| DURANEX® 7307 | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| Lucent PBT TPB-125 | Lucent Polymers, Inc. | PBT | Lucent PBT |
| POCAN® B 4239 000000 | LANXESS Corporation | PBT | POCAN® |