YUCLAIR® FN810
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mmZl3G_YUCLAIR-FN810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUCLAIR FN810 is octene-1 copolymer designed for use in stretch wrap film application. YUCLAIR FN810 provides stronger film than ones made from competitive LLDPE film grades. Therefore YUCLAIR FN810 shows superior tensile strength, tear strength, gel-free, cling property. Outstanding clarity and good processibility make this resin an ideal choice for film application when blended with conventional LDPE. YUCLAIR FN810 can be processed readily into blown film using standard extrusion techniques. YUCLAIR FN810 complies with FDA regulations in 21 CFR177.1520 for all food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | ASTM D746 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.8 | MPa | |
| TD : Yield | 10.8 | MPa | |
| MD : Break | 53.9 | MPa | |
| TD : Break | 49.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break | 700 | % | |
| TD : Break | 800 | % | |
| Spencer Impact | 1.27 | J | ASTM D3420 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1922 | ||
| MD | 176.5 | kN/m | |
| TD | 225.6 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 17 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALEX 01EFR002 - 5230 | AD majoris | PC | MALEX |
| CP PRYME® Polyethylene PE100HDH-8M | Chase Plastics Services Inc. | HDPE | CP PRYME® Polyethylene |
| HAIPLEN EP70 C5 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| LG ASA LI970 | LG Chem Ltd. | ASA | LG ASA |
| ADENE® M38VQEGD00 | A.D. Compound S.p.A. | PP Copolymer | ADENE® |