Mold Max® XLS II
| Category: | Silicone , Silicone |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | Mold Max® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mldNzR_Mold-Max-XLS-II.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mold Max® XLS® II is a Shore 30A tin-catalyzed silicone rubber that exhibits very low long-term shrinkage. XLS® II molds last longer than other silicones in production when casting chemically harsh resins such as epoxies and polyesters as well as urethane foams. Mix ratio is 100A:10B by weight. Pot life is 40 minutes and cure time is 24 hours at room temperature. Mold Max® XLS® II silicone will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making production molds for, reproducing prototypes, furniture, sculpture and architectural elements. Mold Max® XLS® II can be thickened with THI-VEX® II additive for brush-on applications. Mold Max® XLS® II silicone can be used to cast a variety of materials including concrete, wax, gypsum, low melt alloys/metals, epoxy or polyester resins (without using a release agent) and urethane foams. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.820 | cm³/g | ASTM D1475 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio | 100A:10B by weight | ||
| Operating Temperature | -54 to 204 | °C |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.10 | % | ASTM D2566 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 30 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 0.655 | MPa | ASTM D412 |
| Tensile Strength (Break) | 3.79 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 380 | % | ASTM D412 |
| Tear Strength 1 | 19.3 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 0.035 | W/m/K | ASTM D1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 14 | kV/mm | ASTM D149 |
| Dielectric Constant (100 Hz) | 3.40 | ASTM D150 | |
| Dissipation Factor (100 Hz) | 2.0E-3 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 40 | min | ASTM D2471 |
| Thermoset Mix Viscosity | 30000 | cP | ASTM D2393 |
| Demold Time (23°C) | 1400 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 201.3 RC HS Black | RTP Company | Nylon 66 | RTP |
| Niche PA66M40BK | Niche Polymer, LLC | Nylon 66 | Niche |
| Fiberfil® J-60/10/FR | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Firestone C212-15C | Firestone Textiles Company | Nylon 6 | Firestone |
| Karina BEIGE PVC COMPOUND 800-08/52-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |