TRANSMARE® 19HGF30-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mlRGCw_TRANSMARE-19HGF30-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TRANSMARE® 19HGF30-0.001 is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% glass fiber. It is available in Europe for injection molding. Important attributes of TRANSMARE® 19HGF30-0.001 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.5 | g/10 min | |
| 230°C/5.0 kg | 25 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 4.00 mm) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 4.00 mm) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 5700 | MPa | ISO 178 |
| Flexural Stress 2 | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -40°C | 8.5 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 154 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 139 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R633H | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |
| Baytec® MP-080 | Covestro - PUR | PUR-Ether/MDI | Baytec® |
| Jampilen HP510L | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| SEQUEL® 1719HF-UV WHIT | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| ULTEM™ 1100F resin | SABIC Innovative Plastics | PEI | ULTEM™ |