RTP 150 LF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ml0WSU_RTP-150-LF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low Flow - Unreinforced - Flame Retardant - UL94 V-0 |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 to 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.8 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength | 22.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 113 | °C | |
| 1.8 MPa, Unannealed | 65.6 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Melt Temperature | 191 to 232 | °C | |
| Die Temperature | 32.2 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA CT-L03 PLA Melt Strength Enhancer (FDA) | Polyvel Inc. | PLA | Polyvel PLA |
| Smooth-Cast® 320 | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| VESTOLIT® B 6021 Ultra | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| Tuftec™ H1043 | AKelastomers | SEBS | Tuftec™ |
| GETILAN ATP/130 XPE | Crosspolimeri S.p.A. | XLPE | GETILAN |