LNP™ LUBRICOMP™ DFL34 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkGblB_LNPLUBRICOMPDFL34compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound DFL-4034 Product reorder name: DFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 99.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5300 | MPa | ISO 178 |
| Flexural Stress | 147 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 142 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 340 | A. Schulman Europe | ABS | POLYMAN® |
| Sylvin 2990-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TAISOX 7130F | Formosa Plastics Corporation | EVA | TAISOX |
| TOLEN H251 IM | SIBUR, LLC | PP Homopolymer | TOLEN |
| AIE PA6 5010ST | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |