TECHNYL® eXten D 437P NATURAL
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® eXten |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkBryv_TECHNYL-eXten-D-437P-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® eXten D 437P Natural is a high viscosity, unfilled, plasticized, UV and heat stabilized PA6.10 for extrusion applications. Technyl® eXten D 437P is a partially biosourced material. This material is available in natural. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 2.3 | -- | % | |
| Flow | 2.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.65 | -- | % | |
| Saturation, 23°C | 1.9 | -- | % | |
| Molding Shrinkage Isotropy | 1.04 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 890 | 830 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 40.0 | -- | MPa | |
| Break | 50.0 | 11.0 | MPa | |
| Tensile Strain (Break) | 220 | 220 | % | ISO 527-2/1A |
| Flexural Modulus | 720 | 570 | MPa | ISO 178 |
| Flexural Stress | 33.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 3.5 | kJ/m² | |
| 23°C | 25 | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ||||
| -30°C | No Break | No Break | ISO 179/1fU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 215 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 200 to 220 | °C | |
| Cylinder Zone 3 Temp. | 210 to 230 | °C | |
| Cylinder Zone 5 Temp. | 215 to 235 | °C | |
| Die Temperature | 210 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 D83 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Next Nylon 66 Prime Series PXF-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Hanwha Total PP TB52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| INSTRUC PPGF20CC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |
| POLYFORT® FPP 1902 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |