TOPAS® 6013M-07
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Topas Advanced Polymers, Inc. |
| Trademark: | TOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | miYl4w_TOPAS6013M07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Better Surface Appearance |
| General Information | |
|---|---|
| Features |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 63.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 14 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 130 | °C | ISO 75-2/B |
| Glass Transition Temperature 1 | 142 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.530 | ISO 489 | |
| Transmittance (2000 µm) | 91.0 | % | ISO 13468-1 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ateva® 1811 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Europrene® N 2845 GRN | Versalis S.p.A. | NBR | Europrene® |
| Hifax X M1 T11 | LyondellBasell Industries | PP Alloy | Hifax |
| LUVOCOM® 1105-8099 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Lutene® MB9205 | LG Chem Ltd. | LDPE | Lutene® |