Dryflex® SE 50A001
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ELASTO |
| Trademark: | Dryflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mhHRLy_DryflexSE50A001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dryflex SE is our standard TPE range. It is extremely adaptable and can be used advantageously in many applications. The compounds are easy to process and are optimised for injection moulding. We have developed endless formulations to fulfil different properties and application requirements to optimise the finished component. Grades with improved compression set properties, high temperature resistance or more cost efficient values are an essential part of today's wide product spectrum. The Dryflex SE unfilled series is favourable when translucency and good scratch resistance are required, as well as when there are high surface finish requirements. The material enables an easy and secure pigmenting. Unfilled grades have excellent flow and mechanical properties. The low density results in lower weight compared to the filled and semi-filled series. Dryflex SE unfilled compounds are available in hardness from 30 to 90 Shore A in natural and black colours but they can easily be coloured. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 50 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow | ISO 37 | ||
| 100% strain | 1.30 | MPa | ISO 37 |
| 300% strain | 2.00 | MPa | ISO 37 |
| Tensile Stress - Across Flow (Break) | 8.50 | MPa | ISO 37 |
| Tensile Elongation - Across Flow (Break) | 890 | % | ISO 37 |
| Tear Strength 1 | 20 | kN/m | ISO 34-1 |
| Compression Set 2 | ISO 815 | ||
| 23°C, 72 hr | 23 | % | ISO 815 |
| 70°C, 22 hr | 36 | % | ISO 815 |
| 100°C, 22 hr | 59 | % | ISO 815 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 170 - 190 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 200 - 220 | °C | |
| Mold Temperature | 15 - 50 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | C method: crescent sample |
| 2 . | Type B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terlux® HD 2822 | INEOS Styrolution Group GmbH | MABS | Terlux® |
| ASTALAC™ ABS KMZ | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Cheng Yu NGC3 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| EPLAMID 66 GV0 30 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |