MAJORIS CE277 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgqgFp_MAJORIS-CE277---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CE277 - 8229 is a 20% mineral reinforced, elastomer modified compound polypropylene, intended for injection moulding. The product is available in natural (CE277) and black (CE277 - 8229) but other colours can be supplied on request. CE277 - 8229 has a controlled thermal expansion, and provides a good impact/stiffness balance. The product is UV stabilised. CE277 - 8229 gives excellent paint ability by use of adhesive primers alone, or by use of other pre-treatments. APPLICATIONS Automotive exterior:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.70 - 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 57 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 5.8 | kJ/m² | ISO 179/1eA |
| -20°C | 9.4 | kJ/m² | ISO 179/1eA |
| 0°C | 40 | kJ/m² | ISO 179/1eA |
| 23°C | No Break | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 129 | °C | ISO 306/A |
| CLTE - Flow (-30 to 70°C) | 4.0E-5 - 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Additional Information |
|---|
| Paint Adhesion, Peel-test: >20 N/15mm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressureScrew RPM: slow to medium speed |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBB1411 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| UBESTA 3030LUX | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Diakon® Frost 952 51 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| ExxonMobil™ HDPE HD 6714.17 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Pearlthane® CLEAR 15N85 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Pearlthane® |