BJB Epoxy TC-1607 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgituo_BJB-Epoxy-TC-1607-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-1607 A/B is an unfilled, medium viscosity laminating resin for high temperature plastic tooling and part fabrication. This system is ideal for wet lay-up tooling applications where excellent dimensional stability and high mechanical properties are required. Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.200 | g/cm³ | |
| Part B | 1.000 | g/cm³ | |
| Shrinkage 1 | 0.13 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Demold Time | 1.0 | day | |
| Work Time (25°C) 2 | 35.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | 2.10 | Pa·s | |
| Part A : 25°C | 6.50 | Pa·s | |
| Part B : 25°C | 0.185 | Pa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Laminate Service Temperature | 177 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 177°C | 85 to 89 | ||
| Shore D, 25°C | 93 to 97 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 176 | MPa | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 25°C | 15500 | MPa | |
| 177°C | 6890 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 25°C | 335 | MPa | |
| 177°C | 103 | MPa | |
| Compressive Strength | 182 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 166 | °C | DSC |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ASTM D3386 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 20, Mix Ratio by Volume: 24 | ||
| Shelf Life | 52 | wk |
| Note Message | |
|---|---|
| 1 . | 16 plies of 7500 fiberglass cloth laid up at 0° and 45° |
| 2 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| R-master® 92200 | Polimeros Mexicanos s.a. de c.v. | LLDPE | R-master® |
| Vatpol 203 | Vatan Plastik San. Tic. AS | PE, Unspecified | Vatpol |
| AKROMID® B3 GF 30 1 XL black (4366) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| BP Flex D 4107 CU BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| LNP™ VERTON™ MX02795 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |