Ecovio® F2332
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecovio® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mg07WW_Ecovio-F2332.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ecovio® F2332 is our new biodegradable film product containing 18% renewable resources. It is basically a compound of our biodegradable copolyester ecoflex® F Blend and polylactic acid (PLA). Due to its outstanding mechanical strength ecovio® F2332 offers a great down gauging potential needed for thin film applications like garbage bags, organic waste bags, T-shirt bags, agricultural film etc. ecovio® F2332 already contains antiblocking and slip agents required for easy processing on film extrusion and film conversion equipment. ecoflex® F Blend is the continuous phase in the structure of ecovio® F2332 transferring the beneficial film properties of ecoflex® F Blend into the new product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 to 1.26 | g/cm³ | ISO 1183 |
| Apparent Density | 0.78 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 7.00 to 11.0 | cm³/10min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 30 µm, Blown Film | 300 | MPa | |
| TD : 30 µm, Blown Film | 180 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 30 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 30 µm, Blown Film | 30.0 | MPa | |
| MD : 30 µm, Blown Film | 15.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 30 µm, Blown Film | 420 | % | |
| TD : Break, 30 µm, Blown Film | 480 | % | |
| Dart Drop Impact (30 µm, Blown Film) | 650 | g | ASTM D1709A |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 23°C, 50% RH, 30 µm, Blown Film | 120 | g/m²/24 hr | |
| 38°C, 90% RH, 30 µm, Blown Film | 600 | g/m²/24 hr |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | DSC | ||
| -- 1 | 110 to 120 | °C | |
| -- 2 | 140 to 155 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Renewable Content | 18 | % |
| Note Message | |
|---|---|
| 1 . | ecoflex® |
| 2 . | PLA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Caltex PP MB41R | GS Caltex | PP, Unspecified | Caltex PP |
| Ebalta GH 723 / D | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Emulprene® 1028A | INSA | SBR, Emulsion | Emulprene® |
| Huafon JF-S-HS90 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Sylvin 9915-72 White 1538 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |