Retpol® 300 GF HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mfRKWF_Retpol-300-GF-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 300 GF HS is a 30% glass fibre reinforced homopolymer polypropylene compound. It is a low flow injection moulding grade developed for rigid components requiring high heat deflection temperatures, excellent creep resistance and low mould shrinkages. It is stabilized to meet automotive heat ageing requirements of 500hrs at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 113 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 80 | ||
| Shore D, 15 sec, 3.00 mm | 75 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 69.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 5800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 55 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 154 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 141 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® SSD 330 KNF/E NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Moplen S81S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Nirion 1520/M | Soredi S.p.a. | PC | Nirion |
| Hanwha Total PP TI54 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| TECHNYL® A 216 V15 BLACK 21N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |