LNP™ FARADEX™ DS0036I compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ FARADEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | megzmf_LNPFARADEXDS0036Icompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Faradex* DS0036I is a compound based on Polycarbonate resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: High Impact, Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, EMI/RFI Shielding. Also known as: LNP* FARADEX* Compound DS1003FRHIS Product reorder name: DS0036I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow 1 | 0.40 - 0.70 | % | Internal method |
| Vertical flow direction : 24 hours | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2560 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 59.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/5 |
| Fracture 4 | 53.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 4.3 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/5 |
| Fracture 6 | 5.1 | % | ASTM D638 |
| Fracture | 4.0 - 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 7 | 2600 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1800 | J/m | ASTM D4812 |
| 23°C 9 | 70 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 29.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 10 | |||
| 0.45 MPa, unannealed, 64.0mm span | 136 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 125 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 6.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 - 1.0E+6 | ohms·cm | ASTM D257 |
| Static Decay 11 | 10 | msec | FTMS 101B |
| Shielding Effectiveness (3.00 mm) | 40 - 55 | dB | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 93.3 - 121 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPTREE 6001B | POLYROCKS CHEMICAL CO., LTD | PE, Unspecified | POPTREE |
| SCANBLEND FS8 | Polykemi AB | ASA+PC | SCANBLEND |
| VITAMIDE® AI24NT6426 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Fiberfil® M-1492 BK223 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Karina MBPEBD GREEN 4000/ 35-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |