SMOKEGUARD™ III 1096 NATURAL
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | SMOKEGUARD™ III |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | meWgX1_SMOKEGUARD-III-1096-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A LEAD FREE, LOW SMOKE, HIGHLY FLAME RETARDED, SMOKEGUARD™ COMPOUND FOR PLENUM CABLE APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 - 1.68 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw D | 68 - 74 | ASTM D2240 | |
| Shaw D, 15 seconds | 54 - 60 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.381 mm | 17.2 | MPa | ASTM D412 |
| 1.91 mm | 15.2 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 200 | % | ASTM D412 |
| Fracture, 0.381mm | 190 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -1.00 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.50 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.012 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 62 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 | °C | |
| Cylinder Zone 2 Temp. | 154 | °C | |
| Cylinder Zone 3 Temp. | 163 | °C | |
| Cylinder Zone 4 Temp. | 168 | °C | |
| Cylinder Zone 5 Temp. | 168 | °C | |
| Adapter Temperature | 166 | °C | |
| Melt Temperature | 177 - 185 | °C | |
| Die Temperature | 171 | °C | |
| Extruder Screw Compression Ratio | 3.0:1.0 |
| Extrusion instructions |
|---|
| Melt temperature is critical, at temperatures above 370 degrees F foaming may occur. It may be necessary to adjust barrel temp to attain the desired melt temperature Material should be dried prior to use |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Devcon DFense Blok™ | Devcon | Epoxy | Devcon |
| Diaterm® B26 GF25 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 66 | Diaterm® |
| Gallonprene® GP520-5511 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| PALBLEND® R 45 | pal plast GmbH | PC+ABS | PALBLEND® |
| SQUARE® LSR8602-50A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |