LNP™ THERMOCOMP™ OF006A compound
| Category: | PPS , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mdk5Wi_LNPTHERMOCOMPOF006Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP OF-1006 is a compound based on Polyphenylene Sulfide resin containing Glass Fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 157 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 10800 | MPa | ISO 178 |
| Flexural Stress | 238 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2(1.8 MPa, Unannealed, 64.0 mm Span) | 260 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3462 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tenac™-C 3513 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Bapolene® 4082 | Bamberger Polymers, Inc. | PP Homopolymer | Bapolene® |
| Borealis PP BE170MO | Borealis AG | PP Copolymer | Borealis PP |
| 3M™ Dyneon™ Fluoroelastomer FE 5610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |