INNOPOL® PP CS 3-3120
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mdCU22_INNOPOL-PP-CS-3-3120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 3-3120 is a 20 % talcum filled polypropylene compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 3-3120 is recommended for producing injection moulded products where the required property is high strength besides good stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 3.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 210 - 240 | °C | |
| Middle Temperature | 210 - 240 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 15.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 - 100 % of maximum injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® K 395 A | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| NEFTEKHIM PE 2060V (60118) | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Braskem PE HB-0454 | Braskem | HDPE | Braskem PE |
| Axiall PVC 3605 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Karina NATURAL PVC COMPOUND V-150 LT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |