Hostacom PPR 4170L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mcWh37_Hostacom-PPR-4170L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" PPR 4170L is a unfilled polypropylene Homopolymer. UL listing in all colors, UL94 flammability: HB Rating, RTI: 115°C. The product is designed for injection molding of iron parts. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.904 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 3.0 | g/10 min | |
| 230°C/5.0 kg | 12 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | > 50 | % | |
| Flexural Modulus - Secant | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.5 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 15 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Ball Pressure Test 1(135°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.00 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Imp | UL 746 | ||
| 1.00 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Str | UL 746 | ||
| 1.00 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, ALL | HB | ||
| 1.50 mm, ALL | HB | ||
| 3.00 mm, ALL | HB | ||
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 700 | °C | |
| 4.00 mm | 700 | °C |
| Note Message | |
|---|---|
| 1 . | 0.07874016 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-934 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| Monprene® MP-1878B | Teknor Apex Company | TPE | Monprene® |
| Boltaron 9815 | Boltaron Performance Products | PMMA+PVC | Boltaron |
| Karina WHITE COLOR CONCENTRATE MBU 10/1075-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFLAM® HSF 36 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |