Zytel® HTN 51G35HSLR BK420
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mZPnmA_Zytel-HTN-51G35HSLR-BK420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Across Flow : 80°C, 48 hr | 0.0 | -- | % | |
| Flow | 0.20 | -- | % | |
| Flow : 80°C, 48 hr | 0.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 310 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 190 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10500 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 276 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 262 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 5.8E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 33 | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 28 | -- | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExxonMobil™ LLDPE LL 6301 Series Wire & Cable | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Grivory® GV-2 FWA nat | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| PENTAMID A GV25 MC25 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| SCHULABLEND® M/MX 5301 U | A. Schulman Europe | PC+PBT | SCHULABLEND® |
| OTECH PVC PL1001-1UV - Plenum Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |