Versaflex™ OM6360B Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
Versaflex™ OM 6360B is specifically designed to bond to a variety of standard and modified nylon materials, including those which are glass-filled, heat stabilized and/or impact modified. Outstanding Adhesion in Both Two-Shot and Insert Molding Processes Soft, Rubbery Grip Very Easy to Process

General Information
Features	Workability, good Good adhesion
Uses	overmolding Lawn and Garden Equipment Power/other tools
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.09	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.6 - 2.2	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	60		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ASTM D412
100% strain, 23°C ²	1.72	MPa	ASTM D412
300% strain, 23°C ³	2.21	MPa	ASTM D412
Tensile Strength (Break, 23°C)	2.55	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	780	%	ASTM D412
Tear Strength	22.9	kN/m	ASTM D624
Compression Set (23°C, 22 hr)	25	%	ASTM D395B

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	32.5	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Suggested Max Regrind	20	%
Rear Temperature	182 - 204	°C
Middle Temperature	243 - 266	°C
Front Temperature	249 - 271	°C
Nozzle Temperature	254 - 277	°C
Processing (Melt) Temp	249 - 271	°C
Mold Temperature	12.8 - 29.4	°C
Back Pressure	0.00 - 0.552	MPa
Screw Speed	80 - 120	rpm

Injection instructions
Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ OM 6360B with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versaflex™ OM 6360B has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 3 to 5 in/sec1st Stage - Boost Pressure: 300 to 800 psi2nd Stage - Hold Pressure: 0% of BoostHold Time (Thick Part): 0 to 4 secHold Time (Thin Part): 0 to 3 sec

Injection instructions

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ OM 6360B with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versaflex™ OM 6360B has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 3 to 5 in/sec1st Stage - Boost Pressure: 300 to 800 psi2nd Stage - Hold Pressure: 0% of BoostHold Time (Thick Part): 0 to 4 secHold Time (Thin Part): 0 to 3 sec

Note Message
1 .	2 hours
2 .	Mouth die c
3 .	C mould

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versaflex™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mY5ee4_Versaflex-OM6360B.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Tectron H2339	TECTRON Systems Pte Ltd	TPV	Tectron
Wellamid® GF60-66/6 XE-NBK1	Wellman Engineering Resins	Nylon 66/6	Wellamid®
Unichem 1116G-015	Colorite Polymers	PVC, Flexible	Unichem
NITRIFLEX NP-2130	NITRIFLEX	NBR	NITRIFLEX
Hostacom ERC 1122N	LyondellBasell Industries	PP Copolymer	Hostacom