Generic PPA - Carbon Fiber
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXTzdH_Generic-PPA---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPA - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 - 1.50 | g/cm³ | ASTM D792 |
| 23°C | 1.32 - 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.049 - 0.26 | % | ASTM D955 |
| 23°C | 0.050 - 0.80 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.19 - 0.40 | % | ASTM D570 |
| 23°C, 24 hr | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.56 - 2.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 8960 - 34500 | MPa | ASTM D638 |
| 23°C | 11000 - 36200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 152 - 310 | MPa | ASTM D638 |
| Fracture, 23°C | 172 - 287 | MPa | ASTM D638 |
| Fracture, 23°C | 129 - 291 | MPa | ISO 527-2 |
| 23°C | 144 - 292 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.4 - 2.0 | % | ASTM D638 |
| Yield, 23°C | 1.2 - 2.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 1.5 | % | ASTM D638 |
| Fracture, 23°C | 1.2 - 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 7520 - 28000 | MPa | ASTM D790 |
| 23°C | 10000 - 27200 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 196 - 441 | MPa | ASTM D790 |
| 23°C | 187 - 431 | MPa | ISO 178 |
| Coefficient of Friction | 0.13 - 0.36 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 - 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 18 - 61 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 42 - 96 | J/m | ASTM D256 |
| 23°C | 5.5 - 8.1 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 320 - 860 | J/m | ASTM D256 |
| 23°C | 40 - 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 248 - 286 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 249 - 285 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | ASTM D794 |
| CLTE - Flow | |||
| -- | 2.1E-5 - 2.8E-5 | cm/cm/°C | ASTM D696 |
| -- | 2.0E-6 - 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 10 - 1.3E+9 | ohms | ASTM D257 |
| -- | 10 - 1.0E+9 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 10 - 2.5E+6 | ohms·cm | ASTM D257 |
| Insulation Resistance (23°C) | 1.0E+2 - 1.0E+9 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 135 | °C | |
| Drying Time | 4.0 - 16 | hr | |
| Dew Point | -31.7 - -28.9 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 315 - 331 | °C | |
| Middle Temperature | 321 - 333 | °C | |
| Front Temperature | 323 - 338 | °C | |
| Nozzle Temperature | 325 | °C | |
| Processing (Melt) Temp | 315 - 337 | °C | |
| Mold Temperature | 135 - 150 | °C | |
| Injection Pressure | 85.3 - 103 | MPa | |
| Back Pressure | 0.250 - 0.517 | MPa | |
| Screw Speed | 45 - 55 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPA - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2199 X 117875 A | RTP Company | PEI | RTP |
| Tecnoprene® AK6HI NAT001 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| VITAMIDE® BT36WT6427 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Luxus PE 19076 | Luxus Limited | HDPE | Luxus PE |
| Pier One POM AH100-NAT | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |