LNP™ STAT-LOY™ W3000XXJ compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXEXde_LNP-STAT-LOY-W3000XXJ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY W3000XXJ is a compound based on PBT. Added features of this grade include: Anti-Stat, Colorable, Healthcare Also known as: LNP* STAT-LOY* Compound W3000XXJ Product reorder name: W3000XXJ |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.0 to 4.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.23 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.37 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1930 | MPa | ASTM D638 |
| -- | 1890 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 41.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 8.5 | % | ISO 527-2/5 |
| Break 3 | 4.3 | % | ASTM D638 |
| Break | 9.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1940 | MPa | ASTM D790 |
| -- 5 | 1890 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 61 | J/m | ASTM D256 |
| 23°C 6 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 7 | 90 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.70 | J | ASTM D3763 |
| -- | 0.800 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 157 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 54.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.2E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 1.0E+13 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 221 to 232 | °C | |
| Processing (Melt) Temp | 221 to 232 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVAL™ J171B | EVAL Europe nv | EVOH | EVAL™ |
| Flontech® FT-CAF30-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Generic PUR-Ether | Generic | PUR-Ether | Generic |
| GUR® 4170 | Celanese Corporation | UHMWPE | GUR® |
| Karina IVORY PVC COMPOUND 105902-35/ 1-Y-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |