ElectriPlast® EP-SS/PP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mWio0T_ElectriPlast-EP-SS-PP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-SS/PP is a polypropylene product that contains stainless steel fibers. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2290 | MPa | ASTM D638 |
| Tensile Strength (Break) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 19 | % | ASTM D638 |
| Flexural Modulus | 2110 | MPa | ASTM D790 |
| Flexural Strength | 33.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 79 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 370 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 52 | ohms | ESD STM11.11 |
| Volume Resistivity | 16 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 5.0 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 16 | mm/min | UL 94 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 232 | °C | |
| Middle Temperature | 238 | °C | |
| Front Temperature | 238 | °C | |
| Nozzle Temperature | 232 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 1.76 | MPa | |
| Screw Speed | 170 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 500 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO T3002 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Generic PP, High Crystal - Talc | Generic | PP, High Crystal | Generic |
| HiFill® PA6/12 GF33 UV BK001 | Techmer Engineered Solutions | Nylon 612 | HiFill® |
| INLUBE PEIGF20TF15 | Infinity LTL Engineered Compounds | PEI | INLUBE |
| Iupiace® AP6GM2 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |