LG ABS HF388H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mWFwCD_LG-ABS-HF388H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG ABS HF388H is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG ABS HF388H are:
Typical application of LG ABS HF388H: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 to 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 48 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 45.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 5.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2600 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 71.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.0 | °C | ASTM D1525 5 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.010 | % | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 190 to 230 | °C | |
| Front Temperature | 200 to 240 | °C | |
| Nozzle Temperature | 200 to 240 | °C | |
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 0.490 to 1.47 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2320SB | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| CERTENE™ SGM-140 | Muehlstein | PS (GPPS) | CERTENE™ |
| Axiall PVC 8651 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Leona™ FH772 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Sylvin 4240-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |