LNP™ LUBRICOMP™ KL004A compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mW1IRT_LNPLUBRICOMPKL004Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KL004A is a compound based on Acetal Homopolymer resin containing PTFE. Added features include: Internally Lubricated Also known as: LNP* LUBRICOMP* Compound KL-4040D Product reorder name: KL004A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 1.9 - 2.5 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 46.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.22 | ASTM D3702 Modified | |
| With Self-Static | 0.090 | ASTM D3702 Modified | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 157 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 87.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-50283 | Teknor Apex Company | TPE | Medalist® |
| WPP PP PRC25TF4-Black B46051 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| VECTOR® 4211A | Dexco Polymers LP | SIS | VECTOR® |
| GERMAMID 6 B GF 25 S SCHWARZ | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| Sylvin 4260-75UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |