MAJORIS POLYPROPYLENE 30 MS NOIR 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mV1iVW_MAJORIS-POLYPROPYLENE-30-MS-NOIR-8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYPROPYLENE 30 MS NOIR 8229 is a 30% mineral filled polypropylene. It is only available in standard black colour. APPLICATIONS BLACK POLYPROPYLENE 30 MS 8229 is used for various injection applications. It is available in a large variety of colours but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 31.0 | MPa | ISO 527-2/50 |
| Fracture | 14.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | 3350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 74.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tensile Stress at Yield, ISO 527, 50 mm/min: 29 to 33 MpaTensile Stress at Break, ISO 527, 50 mm/min: 13 to 15 MpaFlexural Modulus, ISO 178: 3200 to 3500 Mpa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold-on Pressure: 50 to 70% of the injection pressure. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS2006 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Moplen EP548R | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Amilan® CM1017XL3 | Toray Resin Company | Nylon 6 | Amilan® |
| Excelprene® 8375 RoHS | S&E Specialty Polymers, LLC | PVC, Flexible | Excelprene® |
| POLYFORT® FIPP 15 GFC BM K2258 | A. Schulman Europe | PP Copolymer | POLYFORT® |