Delrin® 527UVE NC010
| Category: | Acetal (POM) Homopolymer , ACETAL RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Delrin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mUbcoF_Delrin-527UVE-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV Stabilized Medium Viscosity Acetal Homopolymer with Very Low Emissions |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.9 | % | |
| Flow | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 17 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 27 | % | ISO 527-2 |
| Flexural Modulus | 3000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 270 | kJ/m² | |
| 23°C | 280 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 93.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 178 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | |
| Transverse | 1.1E-4 | cm/cm/°C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 2.00 | mg/kg | VDA 275 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® PP 2173 | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Wanthane® WHT-1564 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Unipren® Elastomers A3 PRTA010 55A UP305 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Plaslube® PC-50/TF/13/SI/2 | Techmer Engineered Solutions | PC | Plaslube® |
| Europrene Latice® 1142 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |