Moplen EP340K
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mUNeP9_Moplen-EP340K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP340K is a nucleated heterophasic copolymer suitable for injection moulding and thermoforming applications. Moplen EP340K exhibits an outstanding low temperature impact performance and good stiffness combined with a good processability. Moplen EP340K is designed for use in luggage, transport and cold storage crates, sports and leisure equipment, toys and typical consumer components which are subjected to impact and/or low temperature. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.40 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 46.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 0°C | 13 | kJ/m² | |
| 23°C | 66 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 230 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -57.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 52.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALEX 01EFR002 - 4229 | AD majoris | PC | MALEX |
| SABIC® STAMAX 60YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| EvoSource™ PS 3500 | MBA Polymers | PS (GPPS) | EvoSource™ |
| Geon™ Vinyl Flexible R7426A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 4215-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |