COSMOPLENE® FS6612L
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mSxXGc_COSMOPLENE-FS6612L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE FS6612L is Polypropylene Terpolymer product designed for double bubble process with low heat temperature, high transparency and surfact gloss. COSMOPLENE FS6612L is suitable for skin layer when coextruded with LLDPE as core layer for shrink film application. FS6612L contains Antiblocking agent and slip agent. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 44.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 880 | % | ASTM D638 |
| Apparent Bending Modulus | 760 | MPa | ASTM D747 |
| Coefficient of Friction (vs. Itself - Static) | 0.40 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | Internal Method | ||
| MD : 30 µm | 360 | MPa | |
| TD : 30 µm | 370 | MPa | |
| Seal Initiation Temperature (30 µm) | 115 | °C | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 128 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (30.0 µm) | 150 | ASTM D2457 | |
| Haze (30.0 µm) | 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 250 | °C | |
| Take-Off Roll | 26.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostacom TRC 452N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Kazan LDPE 15313-003 OKP 22 1111 2002 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| LNP™ LUBRICOMP™ RFL22E compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| Plexiglas® Satinice df23 7H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| VALOX™ 325 resin | SABIC Innovative Plastics | PBT | VALOX™ |