Durethan® BKV 230 H2.0 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mRkZb5_DurethanBKV230H20DUS008000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.85 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.14 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.35 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.040 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8600 | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 130 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 8.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 7500 | 4400 | MPa | ISO 178/A |
| Flexural Stress 6 | ||||
| 3.5% strain | 205 | 105 | MPa | ISO 178/A |
| 23°C | 210 | 125 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 4.5 | 6.2 | % |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 14 | 15 | kJ/m² | ISO 180/1A |
| 23°C | 23 | 35 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | 75 | kJ/m² | ISO 180/1U |
| 23°C | 75 | 90 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 198 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE Powder 2102P5 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Shuang-Bang AB-205 | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| Borealis PP WE950CF | Borealis AG | Polyolefin, Unspecified | Borealis PP |
| Fainplast PVC CRK 84 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Extreme™ D | Spartech Plastics | TPO | Extreme™ |