| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mRaz0u_Hostacom-65F5-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom 65F5-2 conventional melt flow, 1,500 MPa flexural modulus, 20% calcium carbonate-filled polypropylene homopolymer is designed for high stiffness, excellent chemical resistance and improved surface quality of molded parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 48 hr, 3.20 mm) | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 30.0 | MPa | |
| Break | 13.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 80 | % | |
| Flexural Modulus - Tangent 1 | 1500 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 96.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 107 CC UV | RTP Company | PP, Unspecified | RTP |
| Carbo-Rite™ B-515N | Lubrizol Advanced Materials, Inc. | PS (HIPS) | Carbo-Rite™ |
| Geon™ BIO RB7000 | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| EPO-TEK® H37-MPT | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ LUBRICOMP™ UX06427 compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |