Clearflex® FH 50
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mRS0Y9_Clearflex-FH-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex FH 50 is a linear medium density polyethylene, with antioxidants, suitable for blown film extrusion. Films manufactured with Clearflex FH 50 are characterised by a good balance between toughness and rigidity, have high temperature resistance together with optimum sealing properties. Main Application Due to its high mechanical properties and excellent processability, Clearflex FH 50 is recommended in coextrusion for the production of film having good rigidity. Moreover, its very low gel content makes the resin ideal for lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 25 µm, Blown Film | 450 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 500 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, Blown Film | 16.0 | MPa | |
| TD : Yield, 25 µm, Blown Film | 18.0 | MPa | |
| MD : Break, 25 µm, Blown Film | 35.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm, Blown Film | 650 | % | |
| TD : Break, 25 µm, Blown Film | 750 | % | |
| Dart Drop Impact 1(25 µm, Blown Film) | 50 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 25.0 µm | 8.0 | kN/m | |
| TD : 25.0 µm | 100.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 117 | °C | ISO 306/A |
| Melting Temperature | 128 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 18 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C LT350 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| TRIMID® N6-200N | Polymer Technology and Services, LLC | Nylon 6 | TRIMID® |
| Xuchuan 1065G/B-5009 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyether | Xuchuan |
| ASTADUR™ PBT B4300G6 | Marplex Australia Pty. Ltd. | PBT | ASTADUR™ |
| FHR Polypropylene 23S1Acs256 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |