Alathon® M6080WC
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mPuyg9_Alathon-M6080WC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M6080WC is a natural high density polyethylene homopolymer with a narrow molecular weight distribution formulated for use as primary insulation for coaxial and control cable applications including gas-injected or chemically expanded insulation. This resin provides enhanced processability and stiffness and exhibits excellent color, low odor and good processing stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.958 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.9 | MPa | |
| Break | 21.4 | MPa | |
| Tensile Elongation (Break) | 1900 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 1320 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.36 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 3.0E-5 | ASTM D1531 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 to 163 | °C | |
| Cylinder Zone 2 Temp. | 177 to 204 | °C | |
| Cylinder Zone 3 Temp. | 204 to 232 | °C | |
| Cylinder Zone 4 Temp. | 246 to 260 | °C | |
| Cylinder Zone 5 Temp. | 246 to 260 | °C | |
| Adapter Temperature | 246 to 260 | °C | |
| Melt Temperature | 246 to 260 | °C | |
| Die Temperature | 246 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6002 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| Devlon 6GF30 | Devol® Engineering Polymers | TP, Unspecified | Devlon |
| Latilub 57D-15T G/30 | LATI S.p.A. | Nylon, Unspecified | Latilub |
| MAJORIS FFR307C - 8487 | AD majoris | PP Homopolymer | MAJORIS |
| Delene 1110 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | Delene |