PRE-ELEC® PS 1324
| Category: | PS Alloy , Polystyrene Alloy |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mPQ6Wr_PRE-ELEC-PS-1324.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PS 1324 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity. PRE-ELEC® PS 1324 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extruded sheet for thermoformed ESD trays. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/21.6 kg | 45 | g/10 min | ASTM D1238, ISO 1133 |
| 200°C/5.0 kg | 0.80 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Flow direction | 0.50 - 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A | 99 | ASTM D2240, ISO 868 | |
| Shaw D | 73 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Transverse flow : Yield | 17.9 | MPa | ASTM D638 |
| Flow : Yield | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Transverse flow : Yield | 18.0 | MPa | ISO 527-2 |
| Across Flow | 20.0 | MPa | ASTM D638 |
| Flow | 22.1 | MPa | ASTM D638 |
| -- 1 | 20.0 | MPa | ISO 527-2 |
| -- 2 | 22.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Transverse flow : Yield | 4.0 | % | ASTM D638, ISO 527-2 |
| Flow : Yield | 4.0 | % | ASTM D638, ISO 527-2 |
| Transverse flow : Fracture | 65 | % | ASTM D638 |
| Flow : Fracture | 80 | % | ASTM D638 |
| Fracture 3 | 65 | % | ISO 527-2 |
| Fracture 4 | 80 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1790 | MPa | ASTM D790 |
| 4.00 mm | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -20°C | 8.4 | kJ/m² | ASTM D256 |
| -20°C | 10 | kJ/m² | ISO 179 |
| 23°C | 14 | kJ/m² | ISO 179 |
| 23°C | 13 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 6 | |||
| -20°C | 61 | kJ/m² | ASTM D256 |
| -20°C | 60 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 14.7 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 18.9 | kJ/m² | ASTM D256 |
| Notched Izod Impact 7 | ISO 180 | ||
| -20°C | 14 | kJ/m² | ISO 180 |
| 23°C | 18 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 63.0 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 67.2 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength 8 | ISO 180 | ||
| -20°C | 64 | kJ/m² | ISO 180 |
| 23°C | 67 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 78.9 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 79.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 67.2 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 67.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 97.2 | °C | ASTM D1525 9 |
| -- | 97.0 | °C | ISO 306/A50 |
| Bending test | |||
| -- 10 | > 1.0E+3 | Cycles | |
| -- 11 | > 1.0E+3 | Cycles |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+4 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 220°C |
| Note Message | |
|---|---|
| 1 . | Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 4 mm thickness |
| 8 . | 4 mm thickness |
| 9 . | 速率 A (50°C/h), 载荷2 (50N) |
| 10 . | Across Flow, ISO 5626 |
| 11 . | Flow, ISO 5626 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P598 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| VINIKA® D2151A | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| WELLAMID Nylon 6000 CF 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Wondel® P PM8 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| CALSIN 1300W | Pooya Polymer Tehran | Polyolefin, Unspecified | CALSIN |