| Normal viscosity polyamide 6, modified with 25% PTFE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.5 | -- | % | ISO 294-4 |
| Flow | 1.4 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.8 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2850 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 55.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | 10 | % | ISO 527-2/50 |
| Flexural Modulus | 2600 | -- | MPa | ISO 178 |
| Flexural Stress | 90.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | -- | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.2 mm) | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6, MHRS, 14-030 N , X25 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.18 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 265 - 285 | °C | |
| Middle Temperature | 270 - 295 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 55.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 550100A75 | SO.F.TER. SPA | SBS | Sofprene T® |
| TRIREX® 3027IR | Samyang Corporation | PC | TRIREX® |
| DURACON® M90LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| HAIPLEN EP10 G6 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Karina BLACK PVC COMPOUND 450-48/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |