SABIC® SUPEER™ 8115L
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® SUPEER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mOgOgi_SABICSUPEER8115L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® SUPEER™ 8115L is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE blown film applications and has good processablity. The grade offers better performance in terms of tensile properties, stiffness / toughness ratio and optical properties. Application Typical applications for SABIC® SUPEER™ 8115L are lamination film, frozen bags, liquid pouches, heavy duty bags, industrial liner, agriculture film, stretch hood, surface protective film. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 50 µm, blown film | 136 | MPa | ASTM D882 |
| 1% secant, TD : 50 µm, blown film | 151 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 10.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 52.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 49.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 650 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm, Blown Film) | > 1000 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 15 | g | ASTM D1922 |
| TD : 50 µm, blown film | 24 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | 180 - 200 | °C | |
| Blow-up Ratio | 2.00 - 3.00 | ||
| Properties have been measured on blown film of 50 µm and BUR = 2.5 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Pro® 2505 CU | Multibase, A Dow Corning Company | PP, Unspecified | Multi-Pro® |
| 4PROP® 9D12430 | 4Plas | PP Homopolymer | 4PROP® |
| AEI SX490:CM401 and SX490:CM401-2 | AEI Compounds Limited | LDPE | AEI |
| Ecomax 2000 | KMI Group, Inc. | TPE | Ecomax |
| DAI-EL™ G-7211 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |