Innova R 770E
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Videolar-Innova S/A |
| Trademark: | Innova |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mNn1xi_InnovaR770E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Characteristics:
Process:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.70 | % | ASTM D955 |
| -- | 0.40 - 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation | < 0.10 | % | ASTM D570 |
| Saturated, 23°C | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 70 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2600 | MPa | ASTM D638 |
| 23°C | 2450 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 36.0 | MPa | ASTM D638 |
| Fracture, 23°C | 30.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 50 | % | ASTM D638 |
| Fracture, 23°C | 45 | % | ISO 527-2 |
| Flexural Strength | |||
| 23°C | 52.0 | MPa | ASTM D790 |
| 23°C | 51.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 120 | J/m | ASTM D256 |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Unannealed) | 88.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 2 |
| -- | 97.0 | °C | ASTM D1525, ISO 306/B50 4 3 |
| -- | 100 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 40 - 75 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Note Message | |
|---|---|
| 1 . | 120°C/h |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 20 V25 BLACK 25 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Starpylen HZ 80E7 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Inverko HDPE Regranulaat | Inverko Compounding B.V. | HDPE | Inverko |
| Jampilen HP561S | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| POLYfill PPH GK8020D | Polykemi AB | PP Homopolymer | POLYfill |