DIAREX® THH103
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | DIAREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mNYubB_DIAREX-THH103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DIAREX® THH103 is a General Purpose Polystyrene material. It is available in Asia Pacific. Important attributes of DIAREX® THH103 are:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.7 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, Injection Molded) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, Injection Molded) | 2.6 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 21 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP1B20 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Spartech Polycom 2850-60 | Spartech Polycom | PVC, Unspecified | Spartech |
| Xuchuan 2005L/B-8005 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| Bionate® II 90A | DSM Biomedical Inc. | PC+TPU | Bionate® II |
| EMAC+® SP1307 | Westlake Chemical Corporation | EMA | EMAC+® |