NatureFlex™ NVS 90
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | NatureFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mMYGWQ_NatureFlex-NVS-90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureFlex™ NVS 90 is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of NatureFlex™ NVS 90 include bags/liners, film and packaging. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 23 µm | > 3000 | MPa | |
| 1% Secant, TD : 23 µm | > 1520 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 23 µm | 124 | MPa | |
| TD : Yield, 23 µm | 68.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 23 µm | 22 | % | |
| TD : Break, 23 µm | 70 | % | |
| Seal Strength 2 | 0.12 | N/mm | Internal Method |
| Seal Initiation Temperature (23 µm) | 90.6 to 199 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) (24°C, 23 µm, 0.0% RH) | 3.10 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission 3 | 370 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 23.4 | µm | Internal Method |
| Yield (23.4 µm) | 29.9 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.4 µm) | 110 | ASTM D2457 | |
| Haze 4(23.4 µm) | 4.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Thickness: 0.92 mil |
| 2 . | 275°F, 0.5 secs, 10 psi, thickness: 0.92 mil |
| 3 . | 100°F, 90%RH, thickness: 0.92 mil |
| 4 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8202C HS | BASF Corporation | Nylon 6 | Ultramid® |
| FORMEX® GK-30 | ITW FORMEX | PP, Unspecified | FORMEX® |
| Glastic® UTS 1478 | Glastic Corporation | Polyester, TS | Glastic® |
| Laticonther 62 CPG/500 | LATI S.p.A. | Nylon 6 | Laticonther |
| POLIMAXX 1111NXGA6 | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |