Osterlene® HIPS0302

Category:	PS (HIPS) , High Impact Polystyrene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mLz2OB_OsterleneHIPS0302.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HIPS0302 is a high impact polystyrene designed specifically for extrusion/thermoforming.

The polymer's balanced properties and processing characteristics make it especially suitable for industrial packaging deep draw thermoforming and custom multi-layer sheet extrusion.

This popular resin has established itself as The standard extrusion grade high impact polystyrene.

General Information
Features	Impact resistance, high
Uses	Sheet
Agency Ratings	FDA 21 CFR 177.1640
Processing Method	Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	3.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2070	MPa	ASTM D638
Tensile Strength (Yield)	24.1	MPa	ASTM D638
Tensile Elongation (Break)	55	%	ASTM D638
Flexural Modulus	2210	MPa	ASTM D790
Flexural Strength	47.6	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	110	J/m	ASTM D256
Instrumented Dart Impact	14.1	J	ASTM D3029

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Annealed)	93.9	°C	ASTM D648
Vicat Softening Temperature	98.9	°C	ASTM D1525

Optical	Nominal Value		Test Method
Gardner Gloss (60°)	70		ASTM D523

Resin Grade	Manufacturer	Category	Trademark
Maxelast® P3850	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Telcar® TL-1269A	Teknor Apex Company	TPE	Telcar®
ASTALAC™ ABS M7	Marplex Australia Pty. Ltd.	ABS	ASTALAC™
FRAGOM PR/04 AFKK N	Crosspolimeri S.p.A.	TP, Unspecified	FRAGOM
Karina BLACK PVC COMPOUND 600D48/ 1-C-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina