Order Products : sales@su-jiao.com
LNP™ THERMOCOMP™ DX11354X compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mLsWIu_LNP-THERMOCOMP-DX11354X-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP Compound DX11354X is a colorable PC based compound with stable plating and RF performance, colored LDS material solution, good surface and processing window, high impact strength. It is a general purpose product available in internal and external parts for Laser Direct Structuring applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2400 | MPa | ASTM D638 |
| -- | 2320 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 3 | 45.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/50 |
| Break 5 | 70 | % | ASTM D638 |
| Break | 84 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2380 | MPa | ASTM D790 |
| -- 7 | 2450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 86.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D256 |
| 23°C 9 | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 121 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 117 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 136 | °C | ISO 306/B50, ASTM D1525 11 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (1.00 GHz) | 3.03 | ASTM D150 | |
| Dissipation Factor (1.00 GHz) | 6.6E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 255 to 275 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 140 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*4 mm |
| 11 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecoform® PO20 GR10 NL HS | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| TRIBIT® 1800H | Samyang Corporation | PBT | TRIBIT® |
| Globalprene® 3540F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| INSTRUC PA66GF10 | Infinity LTL Engineered Compounds | Nylon 66 | INSTRUC |
| Sylvin 86040-95FUV Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |