CALIBRE™ 200-10
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mLDrEU_CALIBRE-200-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 200-10 Series are produced in compliance with the US Food and Drug Administration (FDA) and EU food contact regulations. They provide excellent impact resistance, heat distortion resistance and optical clarity. The CALIBRE 200-10 series products are available in 2 additive packages: CALIBRE 200: No mold release or UV Stabilizer. CALIBRE 201: Mold release Govt. and Industry Standards:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.20 | g/cm³ | ISO 1183/A |
| -- | 1200 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50, ISO 527-2 3 3 |
| Tensile Stress | |||
| Yield | 60.0 | MPa | ISO 527-2/50, ISO 527-2 4 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 6.0 | % | ISO 527-2/50, ISO 527-2 5 |
| Break | 150 | % | ISO 527-2/50 |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Flexural Modulus 7 | 2400 | MPa | ISO 178 |
| Flexural Stress 8 | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 9 | ||
| -30°C | 13.0 | kJ/m² | |
| 23°C | 90.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 10 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 88 | kJ/m² | ISO 180/4A |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 144 | °C | ISO 75-2/B |
| 0.45 MPa | 145 | °C | ISO 75-2 11 |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 141 | °C | ISO 75-2/A |
| 1.8 MPa | 131 | °C | ISO 75-2 12 |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 149 | °C | ISO 306 13 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 14 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 15 |
| Electric strength | 17 | kV/mm | IEC 60243-1 16 |
| Relative Permittivity | IEC 60250 17 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 18 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 19 | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 20 | |
| Burning Behav. at thickness h (3.20 mm, UL) | HB | ISO 1210 21 | |
| Oxygen index | 26 | % | ISO 4589-2 22 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.0 to 91.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 2.0 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP531-679UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| RTP 103 AV (20% FOAMED) | RTP Company | PP, Unspecified | RTP |
| Star L PA6 D83 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| ALTECH® PA66 C 2033/509 GF33 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| ALCUDIA® LDPE 2820F | REPSOL | LDPE | ALCUDIA® LDPE |