ENVIROPLAS® ENV13-NC150
| Category: | PC , Polycarbonate |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIROPLAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mIIUMu_ENVIROPLAS-ENV13-NC150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding - Foaming Grade, 10% Fiberglass Reinforced, Non-Brominated/Chlorine-Free Flame Retardant, Impact-Modified, RoHS Compliant NC0150 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV13 Series Products Are Available With Mold Release and/or UV Stabilizer. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 55.2 | MPa | ASTM D638 |
| Flexural Modulus | 2650 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 129 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal method | ||
| 1.50 mm | V-2 | Internal method | |
| 3.00 mm | V-1 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 293 - 310 | °C | |
| Front Temperature | 293 - 310 | °C | |
| Nozzle Temperature | 271 - 293 | °C | |
| Mold Temperature | 73.9 - 102 | °C |
| Injection instructions |
|---|
| Recommended Drying Conditions: 4 hours @ 220 °F for Blowing Agent (Recommended 1.5%) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PR120 | Premier Polymers, LLC. | PP Random Copolymer | Premier |
| Dynaglide® DW 611 | DeWAL Industries | PTFE | Dynaglide® |
| LG PVC LS170 | LG Chem Ltd. | PVC Homopolymer | LG PVC |
| LinGen FR290 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | LinGen |
| EvoSource™ ABS 4535 70/35 | MBA Polymers Austria Kunststoffverarbeitung GmbH | ABS | EvoSource™ |