AKROMID® A3 S3 black (1043)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mI18yE_AKROMID-A3-S3-black-1043-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 S3 black (1043) is an unreinforced and dry impact resistant polyamide 6.6 Applications are connecting and fixing systems in the automotive and elctro industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.5 | -- | % | |
| Flow | 1.2 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.1 | -- | % | ISO 1110 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 93.0 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 67.0 | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2850 | 1600 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 15 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 213 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 67.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 263 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min, DSC |
| 3 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 HS L | RTP Company | Nylon 66 | RTP |
| Spartech Polycom EP5140 A1 | Spartech Polycom | PP Homopolymer | Spartech |
| Globalprene® 1487F | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Sylvin 6185-80 White 1241 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Monprene® MP-3020 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |